| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |||
| 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.35 % @Thickness 2.00 mm |
0.35 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.200 % @Thickness 2.00 mm |
0.200 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Viscosity | 157000 cP @Shear Rate 5000 1/s, Temperature 260 °C |
157000 cP @Shear Rate 5000 1/s, Temperature 500 °F |
ISO 11403-1 -2 | ||
| 193000 cP @Shear Rate 5000 1/s, Temperature 250 °C |
193000 cP @Shear Rate 5000 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 241000 cP @Shear Rate 5000 1/s, Temperature 240 °C |
241000 cP @Shear Rate 5000 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| 408000 cP @Shear Rate 500 1/s, Temperature 260 °C |
408000 cP @Shear Rate 500 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |||
| 530000 cP @Shear Rate 500 1/s, Temperature 250 °C |
530000 cP @Shear Rate 500 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 692000 cP @Shear Rate 500 1/s, Temperature 240 °C |
692000 cP @Shear Rate 500 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527-1/-2 | ||
| Tensile Stress | 5.00 MPa @Strain 0.160 %, Time 3600 sec |
725 psi @Strain 0.160 %, Time 1.00 hour |
isochronous; ISO 11403-1 -2 | ||
| 5.00 MPa @Strain 0.175 %, Time 36000 sec |
725 psi @Strain 0.175 %, Time 10.0 hour |
isochronous; ISO 11403-1 -2 | |||
| 5.00 MPa @Strain 0.177 %, Time 360000 sec |
725 psi @Strain 0.177 %, Time 100 hour |
isochronous; ISO 11403-1 -2 | |||
| 5.00 MPa @Strain 0.210 %, Time 3.60e+6 sec |
725 psi @Strain 0.210 %, Time 1000 hour |
isochronous; ISO 11403-1 -2 | |||
| Elongation at Break | 10 % | 10 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 | ||
| Shear Modulus | 0.120 GPa @Temperature 160 °C |
17.4 ksi @Temperature 320 °F |
Dynamic; ISO 11403-1 -2 | ||
| 0.191 GPa @Temperature 120 °C |
27.7 ksi @Temperature 248 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.419 GPa @Temperature 70.0 °C |
60.8 ksi @Temperature 158 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.17 GPa @Temperature 20.0 °C |
170 ksi @Temperature 68.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.31 GPa @Temperature -20.0 °C |
190 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.43 GPa @Temperature -50.0 °C |
207 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180/1A | ||
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | ISO 180/1U | ||
| 34.0 kJ/m² @Temperature -30.0 °C |
16.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA | ||
| 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 2870 MPa @Pressure 25.0 MPa, Temperature 23.0 °C |
417000 psi @Pressure 3630 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | ||
| 2920 MPa @Pressure 20.0 MPa, Temperature 23.0 °C |
423000 psi @Pressure 2900 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 2970 MPa @Pressure 15.0 MPa, Temperature 23.0 °C |
431000 psi @Pressure 2180 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 3050 MPa @Pressure 10.0 MPa, Temperature 23.0 °C |
442000 psi @Pressure 1450 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 3125 MPa @Pressure 5.00 MPa, Temperature 23.0 °C |
453200 psi @Pressure 725 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 3500 MPa @Time 3600 sec |
508000 psi @Time 1.00 hour |
ISO 899-1 | |||
| Tensile Creep Modulus, 1000 hours | 1500 MPa @Pressure 25.0 MPa, Temperature 23.0 °C |
217000 psi @Pressure 3630 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | ||
| 1640 MPa @Pressure 20.0 MPa, Temperature 23.0 °C |
238000 psi @Pressure 2900 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 1870 MPa @Pressure 15.0 MPa, Temperature 23.0 °C |
271000 psi @Pressure 2180 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 2170 MPa @Pressure 10.0 MPa, Temperature 23.0 °C |
315000 psi @Pressure 1450 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 2380 MPa @Pressure 5.00 MPa, Temperature 23.0 °C |
345000 psi @Pressure 725 psi, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 2400 MPa @Time 3.60e+6 sec |
348000 psi @Time 1000 hour |
ISO 899-1 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0090 @Frequency 100 Hz |
0.0090 @Frequency 100 Hz |
IEC 60250 | ||
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.85 J/g-°C | 0.442 BTU/lb-°F | |||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 195 °C | 383 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 | |||
| Flame Spread | 24 mm/min @Thickness 1.00 mm |
0.94 in/min @Thickness 0.0394 in |
SE/B; ISO 3795 (FMVSS 302) | ||
| Oxygen Index | 22 % | 22 % | ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PBT-GB20< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PBT-GB20 | ||||
| UL recognition | UL | ||||