LCP C230GI 材料說明：液晶聚合物樹脂：sepaz LCP樹脂具有傳統塑料的一種獨特的結構和性能沒有想到的。在sepaz LCP以優異的綜合性能和成型效率。sepaz LCP具有獨特的屬性，產品變得更薄，更大的機械強度。sepaz LCP連接器發現使用，傳感器和其他電子元件和CD提取部分，在復印機和傳真辦公和視聽設備部件。
LCP C230GI 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00 cm/cm | 0.00 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 150.1 MPa | 21770 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Flexural Strength | 183.45 MPa | 26607 psi | ASTM D790 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 |
| Izod Impact, Notched | 2.16 J/cm | 4.04 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm @Thickness 1.60 mm |
610 kV/in @Thickness 0.0630 in |
ASTM D149 |
| Dissipation Factor | 0.029 @Frequency 1.00e+6 Hz |
0.029 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 µm/m-°C @Thickness 1.60 mm |
7.78 µin/in-°F @Thickness 0.0630 in |
ASTM D696 |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Thickness 1.60 mm |
20.0 µin/in-°F @Thickness 0.0630 in |
ASTM D696 |
| Melting Point | 352 °C | 666 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 289 °C | 552 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |