| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | DAM; ISO 1183 | ||
| Viscosity | 82000 cP @Shear Rate 5000 1/s, Temperature 270 °C |
82000 cP @Shear Rate 5000 1/s, Temperature 518 °F |
ISO 11403-1 -2 | ||
| 98500 cP @Shear Rate 5000 1/s, Temperature 250 °C |
98500 cP @Shear Rate 5000 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 110700 cP @Shear Rate 5000 1/s, Temperature 240 °C |
110700 cP @Shear Rate 5000 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| 292700 cP @Shear Rate 500 1/s, Temperature 270 °C |
292700 cP @Shear Rate 500 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |||
| 369700 cP @Shear Rate 500 1/s, Temperature 250 °C |
369700 cP @Shear Rate 500 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 403800 cP @Shear Rate 500 1/s, Temperature 240 °C |
403800 cP @Shear Rate 500 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.026 cm/cm | 0.026 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 50%RH; ISO 527-1/-2 | ||
| 32.0 MPa | 4640 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | >= 50 % | >= 50 % | DAM; Nominal; ISO 527-1/-2 | ||
| >= 50 % | >= 50 % | 50%RH; Nominal; ISO 527-1/-2 | |||
| Elongation at Yield | 12 % | 12 % | DAM; ISO 527-1/-2 | ||
| 30 % | 30 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 0.750 GPa | 109 ksi | 50%RH; ISO 527-1/-2 | ||
| 1.10 GPa | 160 ksi | DAM; ISO 527-1/-2 | |||
| Shear Strength | 0.04481 MPa @Shear Rate 50.0 1/s, Temperature 270 °C |
6.499 psi @Shear Rate 50.0 1/s, Temperature 518 °F |
ISO 11403-1 -2 | ||
| 0.05407 MPa @Shear Rate 50.0 1/s, Temperature 250 °C |
7.842 psi @Shear Rate 50.0 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 0.05737 MPa @Shear Rate 50.0 1/s, Temperature 240 °C |
8.321 psi @Shear Rate 50.0 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| 0.14635 MPa @Shear Rate 500 1/s, Temperature 270 °C |
21.226 psi @Shear Rate 500 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |||
| 0.18485 MPa @Shear Rate 500 1/s, Temperature 250 °C |
26.810 psi @Shear Rate 500 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 0.2019 MPa @Shear Rate 500 1/s, Temperature 240 °C |
29.28 psi @Shear Rate 500 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| 0.410 MPa @Shear Rate 5000 1/s, Temperature 270 °C |
59.5 psi @Shear Rate 5000 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |||
| 0.4925 MPa @Shear Rate 5000 1/s, Temperature 250 °C |
71.43 psi @Shear Rate 5000 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 0.5535 MPa @Shear Rate 5000 1/s, Temperature 240 °C |
80.28 psi @Shear Rate 5000 1/s, Temperature 464 °F |
ISO 11403-1 -2 | |||
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | DAM; ISO 179/1eA | ||
| 8.00 J/cm² | 38.1 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 216 °C | 421 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | DAM; ISO 75-1/-2 | ||
| De |
|||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA612-HI< | ISO 11469 | |||
| Processing | Blow Moulding | ||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA612-HI | ||||
| PA612-HI | ISO 1043 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
概述
PA塑料(尼龍，聚酰胺)，英文名稱:Polyamide
PA的品種繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近幾年開(kāi)發(fā)的半芳香族尼龍PA6T和特種尼龍等很多新品種。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收縮率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型溫度：220-300℃
干燥條件：100-110℃/12小時(shí)
堅(jiān)韌、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃燒鑒別方法：火焰上端黃色，下端藍(lán)色，燃燒后塑料熔滴落，起泡，離火后特殊的羊毛，指甲燒焦味和帶芹菜味
|
尼龍6： |
彈性好，沖擊強(qiáng)度，吸水較大 |
|
尼龍66： |
性能優(yōu)于尼龍6，強(qiáng)度高，耐磨性好 |
|
尼龍610： |
與尼龍66相似，但吸水小，剛度低 |
|
尼龍1010： |
半透明，吸水小。耐寒性較好。適于制作一般機(jī)械零件、減磨耐磨零件、傳動(dòng)零件以及化工、電器、儀表等零件 |
成型性能
1、結(jié)晶料，熔點(diǎn)較高，熔融溫度范圍窄，熱穩(wěn)定性差，料溫超過(guò)300度、滯留時(shí)間超過(guò)30分鐘即分解。較易吸濕，需干燥，含水量不得超過(guò)0.3%。
2、流動(dòng)性好，易溢料。宜用自鎖時(shí)噴嘴，并應(yīng)加熱。
3、成型收縮范圍及收縮率大，方向性明顯，易發(fā)生縮孔、變形等。
4、模溫按塑件壁厚在20～90度范圍內(nèi)選取，注射壓力按注射機(jī)類型、料溫、塑件形狀尺寸、模具澆注系統(tǒng)選定，成型周期按塑件壁厚選定。樹(shù)脂粘度小時(shí)，注射、冷卻時(shí)間應(yīng)取長(zhǎng)，并用白油作脫模劑。
5、模具澆注系統(tǒng)的形式和尺寸，增大流道和澆口尺寸可減少縮水。
聚酰胺的不足之處在于：由于熱膨脹和吸水性所至的尺寸精度不夠，耐酸性差，硬度和彈性模量不夠。經(jīng)改良以后，也是比較優(yōu)秀的工程塑料之一。
應(yīng)用
汽車制造方面
用于制造燃料濾網(wǎng)、燃料過(guò)濾器、罐、捕集器、儲(chǔ)油槽、發(fā)動(dòng)機(jī)汽缸蓋罩、散熱器水缸、平衡旋轉(zhuǎn)軸齒輪。也可用在汽車的電器配件、接線柱等。另外，它還可用作驅(qū)動(dòng)、控制部件等。
電器電子工業(yè)
可用于制造電飯鍋、電動(dòng)吸塵器、高頻電子食品加熱器，電器產(chǎn)品的接線柱、開(kāi)關(guān)和電阻器等。
醫(yī)療器械儀器
用于醫(yī)用輸血管、取血器、輸液器等。PA單絲可做外科手術(shù)縫線、假發(fā)等；另外，電子打字機(jī)的數(shù)字旋轉(zhuǎn)盤(pán)、接線柱、傳動(dòng)齒輪、印刷機(jī)的帶式過(guò)濾片等。
其它方面
用于制作一次性打火機(jī)體、堿性干電池襯墊，摩托車駕駛員的頭盔，辦公機(jī)器外殼，辦公用椅的角輪、座和靠背，冰鞋、釣魚(yú)線等，PA薄膜氣體阻隔性能優(yōu)良，而且耐油性、耐低溫沖擊性、耐穿透性好，可用于肉、火腿腸等冷凍食品的包裝。聚酰胺還可棒材和板材，也作齒輪或其它傳動(dòng)裝置。
上海浩銘塑膠有限公司！本公司承諾，所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營(yíng)銷！
可提供以下報(bào)告：COA（產(chǎn)地證明）SGS（檢測(cè)報(bào)告）MSDS（成分報(bào)告）FDA（食品安全報(bào)告）UL黃卡（出口報(bào)告）正規(guī)發(fā)票！歡迎新老客戶來(lái)電咨詢：
聯(lián)系人：鄧小姐
聯(lián)系電話：13917657923
聯(lián)系QQ:996152797
聯(lián)系郵箱：996152797@qq.com