| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.8 % @Thickness 2.00 mm |
1.8 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 0.700 % @Thickness 2.00 mm |
0.700 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Water Absorption at Saturation | 0.30 % | 0.30 % | DAM; Immersion 24h; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 50%RH; ISO 527-1/-2 | ||
| 168 MPa | 24400 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 3.2 % | 3.2 % | DAM; ISO 527-1/-2 | ||
| 3.2 % | 3.2 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 7.90 GPa | 1150 ksi | 50%RH; ISO 527-1/-2 | ||
| 9.50 GPa | 1380 ksi | DAM; ISO 527-1/-2 | |||
| Flexural Modulus | 7.00 GPa | 1020 ksi | 50%RH; ISO 178 | ||
| 8.20 GPa | 1190 ksi | DAM; ISO 178 | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 50%RH; ISO 180/1A | ||
| 13.0 kJ/m² | 6.19 ft-lb/in² | DAM; ISO 180/1A | |||
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1A | |||
| 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
50%RH; ISO 180/1A | |||
| 11.0 kJ/m² @Temperature -40.0 °C |
5.23 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A | |||
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 50%RH; ISO 180/1U | ||
| 70.0 kJ/m² | 33.3 ft-lb/in² | DAM; ISO 180/1U | |||
| 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1U | |||
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1U | |||
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | DAM; ISO 179/1eU | ||
| 9.00 J/cm² | 42.8 ft-lb/in² | 50%RH; ISO 179/1eU | |||
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | 50%RH; ISO 179/1eA | ||
| 1.30 J/cm² | 6.19 ft-lb/in² | DAM; ISO 179/1eA | |||
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| 1.00 J/cm² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
50%RH; ISO 179/1eA | |||
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C | 9.44 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| 16.0 µm/m-°C @Temperature 55.0 - 160 °C |
8.89 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |||
| 26.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 113 µm/m-°C | 62.8 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| 83.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |||
| 158 µm/m-°C @Temperature 55.0 - 160 °C |
87.8 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |||
| Specific Heat Capacity | 2.13 J/g-°C | 0.509 BTU/lb-°F | |||
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 218 °C | 424 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 65.0 °C | 149 °F | DAM; 10°C/min; ISO 11357-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA612-GF33< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA612-GF33 | ||||
| PA612-GF33 | ISO 1043 | ||||
概述
PA塑料(尼龍，聚酰胺)，英文名稱:Polyamide
PA的品種繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近幾年開發的半芳香族尼龍PA6T和特種尼龍等很多新品種。
物理性能
比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米
成型收縮率：PA6 0.8-2.5% ，PA66 1.5-2.2%
成型溫度：220-300℃
干燥條件：100-110℃/12小時
堅韌、耐磨、耐油、,耐水、抗酶菌、但吸水大
燃燒鑒別方法：火焰上端黃色，下端藍色，燃燒后塑料熔滴落，起泡，離火后特殊的羊毛，指甲燒焦味和帶芹菜味
|
尼龍6： |
彈性好，沖擊強度，吸水較大 |
|
尼龍66： |
性能優于尼龍6，強度高，耐磨性好 |
|
尼龍610： |
與尼龍66相似，但吸水小，剛度低 |
|
尼龍1010： |
半透明，吸水小。耐寒性較好。適于制作一般機械零件、減磨耐磨零件、傳動零件以及化工、電器、儀表等零件 |
成型性能
1、結晶料，熔點較高，熔融溫度范圍窄，熱穩定性差，料溫超過300度、滯留時間超過30分鐘即分解。較易吸濕，需干燥，含水量不得超過0.3%。
2、流動性好，易溢料。宜用自鎖時噴嘴，并應加熱。
3、成型收縮范圍及收縮率大，方向性明顯，易發生縮孔、變形等。
4、模溫按塑件壁厚在20～90度范圍內選取，注射壓力按注射機類型、料溫、塑件形狀尺寸、模具澆注系統選定，成型周期按塑件壁厚選定。樹脂粘度小時，注射、冷卻時間應取長，并用白油作脫模劑。
5、模具澆注系統的形式和尺寸，增大流道和澆口尺寸可減少縮水。
聚酰胺的不足之處在于：由于熱膨脹和吸水性所至的尺寸精度不夠，耐酸性差，硬度和彈性模量不夠。經改良以后，也是比較優秀的工程塑料之一。
應用
汽車制造方面
用于制造燃料濾網、燃料過濾器、罐、捕集器、儲油槽、發動機汽缸蓋罩、散熱器水缸、平衡旋轉軸齒輪。也可用在汽車的電器配件、接線柱等。另外，它還可用作驅動、控制部件等。
電器電子工業
可用于制造電飯鍋、電動吸塵器、高頻電子食品加熱器，電器產品的接線柱、開關和電阻器等。
醫療器械儀器
用于醫用輸血管、取血器、輸液器等。PA單絲可做外科手術縫線、假發等；另外，電子打字機的數字旋轉盤、接線柱、傳動齒輪、印刷機的帶式過濾片等。
其它方面
用于制作一次性打火機體、堿性干電池襯墊，摩托車駕駛員的頭盔，辦公機器外殼，辦公用椅的角輪、座和靠背，冰鞋、釣魚線等，PA薄膜氣體阻隔性能優良，而且耐油性、耐低溫沖擊性、耐穿透性好，可用于肉、火腿腸等冷凍食品的包裝。聚酰胺還可棒材和板材，也作齒輪或其它傳動裝置。