| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D 792 |
| 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.020 - 0.030 cm/cm @Time 86400 sec |
0.020 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.025 cm/cm @Time 86400 sec |
0.025 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.030 cm/cm @Time 86400 sec |
0.020 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.025 cm/cm @Time 86400 sec |
0.025 in/in @Time 24.0 hour |
ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D 638 |
| 52.0 MPa | 7540 psi | ISO 527 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D 638 |
| 52.0 MPa | 7540 psi | ISO 527 | |
| Elongation at Break | 12.9 % | 12.9 % | ISO 527 |
| 38.7 % | 38.7 % | ASTM D 638 | |
| Elongation at Yield | 8.4 % | 8.4 % | ISO 527 |
| 9.0 % | 9.0 % | ASTM D 638 | |
| Tensile Modulus | 2.75 GPa | 399 ksi | 50 mm/min; ASTM D 638 |
| 3.03 GPa | 439 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D 790 |
| 4.30 GPa | 624 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 8.81 J/cm @Temperature 23.0 °C |
16.5 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² @Temperature 23.0 °C |
23.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 118 µm/m-°C @Temperature -40.0 - 40.0 °C |
65.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 119 µm/m-°C @Temperature -40.0 - 40.0 °C |
66.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -40.0 - 40.0 °C |
60.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 108 µm/m-°C @Temperature -40.0 - 40.0 °C |
60.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供應(yīng)原料，品質(zhì)真實(shí),物實(shí)價(jià)廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶(hù)前來(lái)咨詢(xún)：
聯(lián)系人： 夏先生
手 機(jī)：13501802636 021 51131842
QQ ：205730283
郵 箱 ：205730283@qq.com
POM-KS302 圖：