類別：聚合物；熱塑性；聚甲醛（POM）；乙縮醛共聚物，無筋
材料說明：90是修改Celcon共聚甲醛等級。它的目的是提供一個優(yōu)異的耐磨性，韌性和光澤度降低的特點而犧牲許多基本的乙縮醛共聚物的優(yōu)點。
物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527-2/1A |
| Flexural Modulus | 1.44 GPa | 209 ksi | ISO 178 |
| 1.52 GPa | 220 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 °C | 329 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | |
| Mold Temperature | 77.0 - 93.0 °C | 171 - 199 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 hour | 3 hour | |
| Injection Pressure | 75.8 - 110 MPa | 11000 - 16000 psi | |
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，F(xiàn)DA等）！
如您需要提前了解原料產品的相關性能或是需要原料產品的相關報告，請您通過電話或是QQ與我聯(lián)系！
歡迎新老客戶來電或QQ咨詢;
聯(lián)系人：李先生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com