類別：聚合物；熱塑性；聚甲醛（POM）；乙縮醛共聚物，聚四氟乙烯填充
材料說明：是一種基于lw90f5 M90縮醛共聚物四氟乙烯填料配制。它是專為使用在對塑料，金屬，玻璃或陶瓷配合表面的磨損應用，在硅橡膠不能容忍。
物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527-2/1A |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.20 kJ/m² | 2.00 ft-lb/in² | ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | |
| Mold Temperature | 77.0 - 93.0 °C | 171 - 199 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 hour | 3 hour | |
| Injection Pressure | 75.8 - 110 MPa | 11000 - 16000 psi | |
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！
我司所銷售所有產品均為原廠原包，均可提供相關資料報告（如：物性表，MSDS報告，UL報告，COA報告，SGS報告，FDA等）！
如您需要提前了解原料產品的相關性能或是需要原料產品的相關報告，請您通過電話或是QQ與我聯系！
歡迎新老客戶來電或QQ咨詢;
聯系人：李先生
聯系電話；13636696005
聯系QQ；1020580970
聯系郵箱；1020580970@qq.com