| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D 792 |
| 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.47 % | 0.47 % | 23°C / 50% RH; ISO 62 |
| 0.33 % @Time 86400 sec |
0.33 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 24.8 % | 24.8 % | 5 mm/min; ISO 527 |
| 32 % | 32 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 22.3 % | 22.3 % | Type I, 5 mm/min; ASTM D 638 |
| 24.8 % | 24.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.98 GPa | 432 ksi | 1 mm/min; ISO 527 |
| 3.21 GPa | 466 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 69.0 MPa | 10000 psi | ISO 178 |
| Flexural Modulus | 2.63 GPa | 381 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.68 GPa | 389 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.710 J/cm @Temperature 23.0 °C |
1.33 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 15.1 J/cm @Temperature 23.0 °C |
28.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 83.0 kJ/m² @Temperature 23.0 °C |
39.5 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.30 | 0.30 | ASTM D 3702 Modified |
| K (wear) Factor | 220 x 10-8 mm³/N-M | 109 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 97.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
54.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 96.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
53.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 162 °C @Thickness 3.20 mm |
324 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司，供應原料，品質真實,物實價廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯系人： 夏先生
手 機：13501802636 021 51131842
QQ ：205730283
郵 箱 ：205730283@qq.com
POM-KI001A 圖：