顆粒圖：
、
、用途：
廣泛應(yīng)用于機(jī)械、儀器儀表、汽車部件、電子電氣、鐵路、家電、通訊、紡機(jī)、體育休閑用品、油管、油箱及一些精密工程制品。
電子電器：連接器、卷線軸、計時器、護(hù)蓋斷路器、開關(guān)殼座。
汽車： 散熱風(fēng)扇、門把、油箱蓋、進(jìn)氣隔柵、水箱護(hù)蓋、燈座。
工業(yè)零件：椅座、自行車輸框、溜冰鞋底座、紡織梭、踏板、滑輸。
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.60 % | 2.60 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | cond; ISO 527-1/-2 |
| 210 MPa | 30500 psi | dry; ISO 527-1/-2 | |
| 90.0 MPa @Temperature 200 °C |
13100 psi @Temperature 392 °F |
ISO 527-1/-2 | |
| 95.0 MPa @Temperature 180 °C |
13800 psi @Temperature 356 °F |
ISO 527-1/-2 | |
| 110 MPa @Temperature 160 °C |
16000 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 125 MPa @Temperature 120 °C |
18100 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | cond; ISO 527-1/-2 | |
| 5.5 % @Temperature 120 °C |
5.5 % @Temperature 248 °F |
ISO 527-1/-2 | |
| 5.5 % @Temperature 160 °C |
5.5 % @Temperature 320 °F |
ISO 527-1/-2 | |
| 5.5 % @Temperature 180 °C |
5.5 % @Temperature 356 °F |
ISO 527-1/-2 | |
| 5.5 % @Temperature 200 °C |
5.5 % @Temperature 392 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | dry; ISO 527-1/-2 | |
| 4.50 GPa @Temperature 200 °C |
653 ksi @Temperature 392 °F |
ISO 527-1/-2 | |
| 4.70 GPa @Temperature 180 °C |
682 ksi @Temperature 356 °F |
ISO 527-1/-2 | |
| 5.00 GPa @Temperature 160 °C |
725 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 5.50 GPa @Temperature 120 °C |
798 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | cond; ISO 178 |
| 9.00 GPa | 1310 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 550 V | 550 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
|