顆粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.85 % | 1.85 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | cond; ISO 527-1/-2 |
| 250 MPa | 36300 psi | dry; ISO 527-1/-2 | |
| 135 MPa @Temperature 160 °C |
19600 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 150 MPa @Temperature 120 °C |
21800 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 2.2 % | 2.2 % | dry; ISO 527-1/-2 |
| 3.5 % | 3.5 % | cond; ISO 527-1/-2 | |
| 3.5 % @Temperature 120 °C |
3.5 % @Temperature 248 °F |
ISO 527-1/-2 | |
| 3.5 % @Temperature 160 °C |
3.5 % @Temperature 320 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | cond; ISO 527-1/-2 |
| 16.0 GPa | 2320 ksi | dry; ISO 527-1/-2 | |
| 10.0 GPa @Temperature 160 °C |
1450 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 11.0 GPa @Temperature 120 °C |
1600 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | cond; ISO 178 |
| 15.0 GPa | 2180 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU |
| 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 450 V | 450 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
|
廣泛用于制造機械、汽車、化學(xué)與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包層等。亦可制成薄膜用作包裝材料。此外，還可用于制作醫(yī)療器械、體育用品、日用品等。