| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.20 % | 2.20 % | Sim. To ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | cond; ISO 527-1/-2 |
| 240 MPa | 34800 psi | dry; ISO 527-1/-2 | |
| 60.0 MPa @Temperature 200 °C |
8700 psi @Temperature 392 °F |
ISO 527-1/-2 | |
| 75.0 MPa @Temperature 180 °C |
10900 psi @Temperature 356 °F |
ISO 527-1/-2 | |
| 90.0 MPa @Temperature 160 °C |
13100 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 2.4 % | 2.4 % | dry; ISO 527-1/-2 |
| 6.3 % | 6.3 % | cond; ISO 527-1/-2 | |
| 7.5 % @Temperature 120 °C |
7.5 % @Temperature 248 °F |
ISO 527-1/-2 | |
| 8.5 % @Temperature 160 °C |
8.5 % @Temperature 320 °F |
ISO 527-1/-2 | |
| 9.0 % @Temperature 180 °C |
9.0 % @Temperature 356 °F |
ISO 527-1/-2 | |
| 9.5 % @Temperature 200 °C |
9.5 % @Temperature 392 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | cond; ISO 527-1/-2 |
| 17.0 GPa | 2470 ksi | dry; ISO 527-1/-2 | |
| 4.50 GPa @Temperature 200 °C |
653 ksi @Temperature 392 °F |
ISO 527-1/-2 | |
| 5.60 GPa @Temperature 180 °C |
812 ksi @Temperature 356 °F |
ISO 527-1/-2 | |
| 6.10 GPa @Temperature 160 °C |
885 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 6.90 GPa @Temperature 120 °C |
1000 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | cond; ISO 178 |
| 17.0 GPa | 2470 ksi | dry; ISO 178 | |
| 4.50 GPa @Temperature 200 °C |
653 ksi @Temperature 392 °F |
ISO 178 | |
| 5.60 GPa @Temperature 180 °C |
812 ksi @Temperature 356 °F |
ISO 178 | |
| 6.10 GPa @Temperature 160 °C |
885 ksi @Temperature 320 °F |
ISO 178 | |
| 6.90 GPa @Temperature 120 °C |
1000 ksi @Temperature 248 °F |
ISO 178 | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 9.50 J/cm² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 282 °C | 540 °F | 10°C/min; ISO 11357-1/-3 |
廣泛用于制造機械、汽車、化學(xué)與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風(fēng)扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包層等。亦可制成薄膜用作包裝材料。此外，還可用于制作醫(yī)療器械、體育用品、日用品等。