顆粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.20 % | 2.20 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | cond; ISO 527-1/-2 |
| 230 MPa | 33400 psi | dry; ISO 527-1/-2 | |
| 100 MPa @Temperature 200 °C |
14500 psi @Temperature 392 °F |
ISO 527-1/-2 | |
| 105 MPa @Temperature 180 °C |
15200 psi @Temperature 356 °F |
ISO 527-1/-2 | |
| 115 MPa @Temperature 160 °C |
16700 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 130 MPa @Temperature 120 °C |
18900 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | cond; ISO 527-1/-2 | |
| 6.5 % @Temperature 120 °C |
6.5 % @Temperature 248 °F |
ISO 527-1/-2 | |
| 6.5 % @Temperature 160 °C |
6.5 % @Temperature 320 °F |
ISO 527-1/-2 | |
| 6.5 % @Temperature 180 °C |
6.5 % @Temperature 356 °F |
ISO 527-1/-2 | |
| 6.5 % @Temperature 200 °C |
6.5 % @Temperature 392 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 8.00 GPa | 1160 ksi | cond; ISO 527-1/-2 |
| 13.0 GPa | 1890 ksi | dry; ISO 527-1/-2 | |
| 5.30 GPa @Temperature 200 °C |
769 ksi @Temperature 392 °F |
ISO 527-1/-2 | |
| 5.70 GPa @Temperature 180 °C |
827 ksi @Temperature 356 °F |
ISO 527-1/-2 | |
| 6.10 GPa @Temperature 160 °C |
885 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 6.90 GPa @Temperature 120 °C |
1000 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | cond; ISO 178 |
| 11.5 GPa | 1670 ksi | dry; ISO 178 | |
| 5.20 GPa @Temperature 160 °C |
754 ksi @Temperature 320 °F |
ISO 178 | |
| 5.80 GPa @Temperature 120 °C |
841 ksi @Temperature 248 °F |
ISO 178 | |
| Izod Impact Resistance | 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
cond; ISO 180/1A |
| 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
dry; ISO 180/1A | |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 180/1A | |
| 2.10 J/cm² @Temperature 23.0 °C |
9.99 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 180/1A | |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU |
| 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 2.10 J/cm² @Temperature 23.0 °C |
9.99 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | cond; IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 400 V | 400 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 159 °C | 318 °F | 5000 hours Thermal Index; IEC 60216/ISO 527-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
|
廣泛用于制造機械、汽車、化學與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包層等。亦可制成薄膜用作包裝材料。此外，還可用于制作醫療器械、體育用品、日用品等。