、用途：
廣泛應(yīng)用于機(jī)械、儀器儀表、汽車部件、電子電氣、鐵路、家電、通訊、紡機(jī)、體育休閑用品、油管、油箱及一些精密工程制品。
電子電器：連接器、卷線軸、計(jì)時(shí)器、護(hù)蓋斷路器、開關(guān)殼座。
汽車： 散熱風(fēng)扇、門把、油箱蓋、進(jìn)氣隔柵、水箱護(hù)蓋、燈座。
工業(yè)零件：椅座、自行車輸框、溜冰鞋底座、紡織梭、踏板、滑輸。
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 3.70 % | 3.70 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | cond; ISO 527-1/-2 |
| 100 MPa | 14500 psi | dry; ISO 527-1/-2 | |
| 30.0 MPa @Temperature 200 °C |
4350 psi @Temperature 392 °F |
ISO 527-1/-2 | |
| 35.0 MPa @Temperature 180 °C |
5080 psi @Temperature 356 °F |
ISO 527-1/-2 | |
| 40.0 MPa @Temperature 160 °C |
5800 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 50.0 MPa @Temperature 120 °C |
7250 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 40 % | 40 % | dry; ISO 527-1/-2 |
| >= 50 % | >= 50 % | cond; ISO 527-1/-2 | |
| >= 50 % @Temperature 120 °C |
>= 50 % @Temperature 248 °F |
ISO 527-1/-2 | |
| >= 50 % @Temperature 160 °C |
>= 50 % @Temperature 320 °F |
ISO 527-1/-2 | |
| >= 50 % @Temperature 180 °C |
>= 50 % @Temperature 356 °F |
ISO 527-1/-2 | |
| >= 50 % @Temperature 200 °C |
>= 50 % @Temperature 392 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 1.00 GPa | 145 ksi | cond; ISO 527-1/-2 |
| 3.30 GPa | 479 ksi | dry; ISO 527-1/-2 | |
| 0.500 GPa @Temperature 200 °C |
72.5 ksi @Temperature 392 °F |
ISO 527-1/-2 | |
| 0.600 GPa @Temperature 180 °C |
87.0 ksi @Temperature 356 °F |
ISO 527-1/-2 | |
| 0.650 GPa @Temperature 160 °C |
94.3 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Flexural Modulus | 0.900 GPa | 131 ksi | cond; ISO 178 |
| 3.30 GPa | 479 ksi | dry; ISO 178 | |
| 0.600 GPa @Temperature 160 °C |
87.0 ksi @Temperature 320 °F |
ISO 178 | |
| 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 178 | |
| Izod Impact Resistance | 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
cond; ISO 180/1A |
| 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
dry; ISO 180/1A | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 180/1A | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 180/1A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | cond; IEC 60243-1 |
| 25.0 kV/mm | 635 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 85.0 µm/m-°C | 47.2 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 128 °C | 262 °F | 5000 hours Thermal Index; IEC 60216/ISO 527-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
|
上海松翰塑化科技有限公司，供應(yīng)原料，品質(zhì)真實(shí),物實(shí)價(jià)廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯(lián)系人： 夏先生
手 機(jī)：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com