顆粒樣圖：
物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183/A | ||
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec |
0.70 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 Type 1A | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527 type 1 A | ||
| Elongation at Break | 15 % | 15 % | ISO 527 Type 1A | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A | ||
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 | ||
| Flexural Modulus | 4.70 GPa | 682 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 5.00e+13 ohm | 5.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 | ||
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 | ||
| Melting Point | 263 °C | 505 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | ||
| Oxygen Index | 26 % | 26 % | ISO 4589 | ||
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 270-280°C | ||||
應用：廣泛用于制造機械、汽車、化學與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包內層等。