物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183/A | ||
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.0066 cm/cm | 0.0066 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0101 cm/cm | 0.0101 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A | ||
| 150 MPa | 21800 psi | ASTM D638 | |||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A | ||
| 2.0 % | 2.0 % | ASTM D638 | |||
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| 220 MPa | 31900 psi | ASTM D790 | |||
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 | ||
| 9.60 GPa | 1390 ksi | ASTM D790 | |||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 263 °C | 505 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75/Af | ||
| 240 °C | 464 °F | ASTM D648 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 270-280°C | ||||
| Draw-plate temperatures | 280-290°C | ||||
用途：
廣泛應用于機械、儀器儀表、汽車部件、電子電氣、鐵路、家電、通訊、紡機、體育休閑用品、油管、油箱及一些精密工程制品。
電子電器：連接器、卷線軸、計時器、護蓋斷路器、開關殼座。
汽車： 散熱風扇、門把、油箱蓋、進氣隔柵、水箱護蓋、燈座。
工業零件：椅座、自行車輸框、溜冰鞋底座、紡織梭、踏板、滑輸。