顆粒：
物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec |
1.3 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | ||
| 1.5 % @Temperature 100 °C, Time 1800 sec |
1.5 % @Temperature 212 °F, Time 0.500 hour |
ISO 62 | |||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 Type 1A | ||
| Tensile Stress | 59.0 MPa @Strain 2.00 % |
8560 psi @Strain 2.00 % |
|||
| 81.0 MPa @Strain 4.00 % |
11700 psi @Strain 4.00 % |
||||
| 83.0 MPa @Strain 6.00 % |
12000 psi @Strain 6.00 % |
||||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ASTM D638 | ||
| 88.0 MPa | 12800 psi | ISO 527 type 1 A | |||
| Elongation at Break | 20 % | 20 % | ISO 527 Type 1A | ||
| 30 % | 30 % | ASTM D638 | |||
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 125 MPa | 18100 psi | ASTM D790 | ||
| 130 MPa | 18900 psi | ISO 178 | |||
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 | ||
| 3.50 GPa | 508 ksi | ASTM D790 | |||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1A | ||
| 80.0 kJ/m² | 38.1 ft-lb/in² | ASTM D256 | |||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1U | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.430 J/cm² | 2.05 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 263 °C | 505 °F | ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75/Af | ||
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 | ||
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
1210 | |||
| Oxygen Index | 26 % | 26 % | ISO 4589 | ||
| Glow Wire Test | 650 °C @Thickness 0.800 mm |
1200 °F @Thickness 0.0315 in |
ISO 60695-2-12 | ||
| 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 | |||
| 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
Ignition Temperature; ISO 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 270-280°C | ||||
| Mixing Zone | 280-290°C | ||||
廣泛用于制造機(jī)械、汽車、化學(xué)與電氣裝置的零件，如齒輪、滾子、滑輪、輥軸、泵體中葉輪、風(fēng)扇葉片、高壓密封圍、閥座、墊片、襯套、各種把手、支撐架、電線包層等。亦可制成薄膜用作包裝材料。此外，還可用于制作醫(yī)療器械、體育用品、日用品等。
上海松翰塑化科技有限公司，供應(yīng)原料，品質(zhì)真實(shí),物實(shí)價(jià)廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
歡迎各位客戶前來咨詢：
聯(lián)系人： 夏先生
手 機(jī)：13501802636
QQ ：205730283
郵 箱 ：205730283@qq.com