特點：
1、綜合性能較好，沖擊強度較高，化學穩定性，電性能良好.
2、與372有機玻璃的熔接性良好，制成雙色塑件，且可表面鍍鉻，噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強、透明等級別。
4、流動性比HIPS差一點，比PMMA、PC等好，柔韌性好。
5、用途：適于制作一般機械零件，減磨耐磨零件，傳動零件和電訊零件.
6、同PVC（聚氯乙烯）一樣在屈折處會出現白化現象。
典型應用范圍:
汽車內外飾：儀表板，飾柱，儀表前蓋，格柵，內外飾件 2.商務設備機殼和內置部件：筆記本/臺式電腦，復印機，打印機，繪圖儀，顯示器 3.電信，移動電話外殼，附件以及智能卡（SIM卡）： 4.電器產品，電子產品外殼，電表罩和殼體，家用開關，插頭和插座，電纜電線管道 5.家用電器，如洗衣機，吹風機，微波爐內外部件等。
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | With Flow; ISO 2577 | ||
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | Across Flow; ISO 2577 | |||
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 240 °C |
20 g/10 min @Load 11.0 lb, Temperature 464 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Elongation at Yield | 4.5 % | 4.5 % | ISO/R527 | ||
| Flexural Strength | <= 85.0 MPa | <= 12300 psi | ISO 178 | ||
| Flexural Modulus | 2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
ISO 178 | ||
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -20.0 °C |
9.52 ft-lb/in² @Temperature -4.00 °F |
ISO 179 | ||
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | 120°C/h; ISO 75/1 | ||
| Vicat Softening Point | 105 °C @Load 5.001 kg |
221 °F @Load 11.03 lb |
50°C/h; ISO 306 | ||
| Flammability, UL94 | V-2 @Thickness 2.50 mm |
V-2 @Thickness 0.0984 in |
|||
| Glow Wire Test | 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
IEC 695-2-1 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Dry Time | 2 - 8 hour | 2 - 8 hour | in circulation dryer | ||
| 2 - 8 hour | 2 - 8 hour | in fresh-air dryer | |||
| 2 - 8 hour | 2 - 8 hour | in desiccant air dryer | |||
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |||
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi | |||
| De |
|||||
| Holding Pressure () | 20-50 | % of injection pressure | |||
| Injection Speed () | High | ||||