- 熔體流動速率 [g/10min]: 3.96
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 0.214
- 拉伸強度 [MPa]: 89.6
- 斷裂伸長率 [%]: 24.1
- 彎曲強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 3.50
- 硬度: 120.0
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 - 1.65 g/cc | 0.0444 - 0.0596 lb/in3 | Average value: 1.33 g/cc Grade Count:60 |
| Filler Content | 0.000 - 30.0 % | 0.000 - 30.0 % | Average value: 6.00 % Grade Count:5 |
| Water Absorption | 0.0500 - 0.500 % | 0.0500 - 0.500 % | Average value: 0.198 % Grade Count:29 |
| Moisture Absorption at Equilibrium | 0.100 - 0.500 % | 0.100 - 0.500 % | Average value: 0.289 % Grade Count:14 |
| Water Absorption at Saturation | 0.350 - 1.65 % | 0.350 - 1.65 % | Average value: 0.582 % Grade Count:17 |
| Particle Size | 10.0 - 70.0 μm | 10.0 - 70.0 μm | Average value: 35.0 μm Grade Count:3 |
| Viscosity | 90000 - 450000 cP | 90000 - 450000 cP | Average value: 244000 cP Grade Count:5 |
| 100000 - 500000 cP @Temperature 400 - 400 °C | 100000 - 500000 cP @Temperature 752 - 752 °F | Average value: 307000 cP Grade Count:9 | |
| Linear Mold Shrinkage | 0.00300 - 0.0180 cm/cm | 0.00300 - 0.0180 in/in | Average value: 0.00959 cm/cm Grade Count:22 |
| Linear Mold Shrinkage, Transverse | 0.00900 - 0.0130 cm/cm | 0.00900 - 0.0130 in/in | Average value: 0.0121 cm/cm Grade Count:11 |
| Melt Flow | 3.96 - 91.0 g/10 min | 3.96 - 91.0 g/10 min | Average value: 28.1 g/10 min Grade Count:9 |
| Spiral Flow | 7.60 - 850 cm | 2.99 - 335 in | Average value: 199 cm Grade Count:9 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85.0 - 109 | 85.0 - 109 | Average value: 101 Grade Count:20 |
| Hardness, Rockwell R | 120 - 127 | 120 - 127 | Average value: 124 Grade Count:7 |
| Hardness, Shore D | 62.0 - 89.0 | 62.0 - 89.0 | Average value: 85.1 Grade Count:15 |
| Ball Indentation Hardness | 90.0 - 230 MPa | 13100 - 33400 psi | Average value: 192 MPa Grade Count:8 |
| Tensile Strength, Ultimate | 80.0 - 150 MPa | 11600 - 21800 psi | Average value: 102 MPa Grade Count:36 |
| Tensile Strength, Yield | 89.6 - 140 MPa | 13000 - 20300 psi | Average value: 102 MPa Grade Count:26 |
| Elongation at Break | 1.50 - 60.0 % | 1.50 - 60.0 % | Average value: 23.7 % Grade Count:57 |
| Elongation at Yield | 2.00 - 6.00 % | 2.00 - 6.00 % | Average value: 4.40 % Grade Count:8 |
| Modulus of Elasticity | 2.20 - 12.0 GPa | 319 - 1740 ksi | Average value: 4.54 GPa Grade Count:53 |
| Flexural Yield Strength | 24.1 - 210 MPa | 3500 - 30500 psi | Average value: 159 MPa Grade Count:51 |
| 9.00 - 95.0 MPa @Temperature 125 - 275 °C | 1310 - 13800 psi @Temperature 257 - 527 °F | Average value: 39.3 MPa Grade Count:6 | |
| Flexural Modulus | 3.50 - 11.1 GPa | 508 - 1610 ksi | Average value: 4.69 GPa Grade Count:48 |
| 0.20312 - 0.20312 GPa @Temperature 204 - 204 °C | 29.460 - 29.460 ksi @Temperature 400 - 400 °F | Average value: 0.203 GPa Grade Count:1 | |
| Compressive Yield Strength | 31.0 - 183 MPa | 4500 - 26500 psi | Average value: 108 MPa Grade Count:24 |
| 65.0 - 70.0 MPa @Temperature 120 - 120 °C | 9430 - 10200 psi @Temperature 248 - 248 °F | Average value: 69.2 MPa Grade Count:6 | |
| Compressive Modulus | 2.48 - 4.14 GPa | 360 - 600 ksi | Average value: 3.31 GPa Grade Count:7 |
| Shear Strength | 53.0 - 80.0 MPa | 7690 - 11600 psi | Average value: 64.1 MPa Grade Count:5 |
| 14.3411 - 68.2581 MPa @Temperature 65.6 - 288 °C | 2080.00 - 9900.02 psi @Temperature 150 - 550 °F | Average value: 43.8 MPa Grade Count:1 | |
| Izod Impact, Notched | 0.214 - 1.07 J/cm | 0.400 - 2.00 ft-lb/in | Average value: 0.518 J/cm Grade Count:24 |
| Izod Impact, Unnotched | 2.70 J/cm - NB | 5.06 ft-lb/in - NB | Average value: 15.8 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 0.450 - 9.50 kJ/m2 | 0.214 - 4.52 ft-lb/in2 | Average value: 4.63 kJ/m2 Grade Count:20 |
| Izod Impact, Unnotched (ISO) | NB | NB | Grade Count:20 |
| Charpy Impact Unnotched | 1.40 J/cm2 - NB | 6.66 ft-lb/in2 - NB | Average value: 15.7 J/cm2 Grade Count:11 |
| Charpy Impact, Notched | 0.0800 - 8.00 J/cm2 | 0.381 - 38.1 ft-lb/in2 | Average value: 1.31 J/cm2 Grade Count:15 |
| Coefficient of Friction | 0.110 - 0.500 | 0.110 - 0.500 | Average value: 0.263 Grade Count:15 |
| K (wear) Factor | 40.3 - 755 x 10-8 mm3/N-M | 20.0 - 375 x 10-10 in3-min/ft-lb-hr | Average value: 612 x 10-8 mm3/N-M Grade Count:5 |
| Limiting Pressure Velocity | 0.210 - 0.660 MPa-m/sec | 6000 - 18800 psi-ft/min | Average value: 0.400 MPa-m/sec Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 4.10e+10 - 4.90e+16 ohm-cm | 4.10e+10 - 4.90e+16 ohm-cm | Average value: 9.18e+15 ohm-cm Grade Count:31 |
| 1.00e+9 - 1.00e+15 ohm-cm @Temperature 125 - 275 °C | 1.00e+9 - 1.00e+15 ohm-cm @Temperature 257 - 527 °F | Average value: 5.00e+14 ohm-cm Grade Count:6 | |
| Surface Resistance | 1.00e+6 - 1.80e+15 ohm | 1.00e+6 - 1.80e+15 ohm | Average value: 1.40e+14 ohm Grade Count:17 |
| Dielectric Constant | 2.80 - 10.9 | 2.80 - 10.9 | Average value: 3.51 Grade Count:27 |
| 4.50 - 4.50 @Temperature 200 - 200 °C | 4.50 - 4.50 @Temperature 392 - 392 °F | Average value: 4.50 Grade Count:1 | |
| 4.50 - 4.50 @Frequency 50000 - 50000 Hz | 4.50 - 4.50 @Frequency 50000 - 50000 Hz | Average value: 4.50 Grade Count:1 | |
| Dielectric Strength | 15.7 - 126 kV/mm | 400 - 3200 kV/in | Average value: 24.2 kV/mm Grade Count:25 |
| Dissipation Factor | 0.00100 - 0.518 | 0.00100 - 0.518 | Average value: 0.0282 Grade Count:25 |
| Comparative Tracking Index | 150 V | 150 V | Average value: 150 V Grade Count:13 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.4 - 150 μm/m-°C | 6.33 - 83.3 μin/in-°F | Average value: 49.4 μm/m-°C Grade Count:30 |
| 22.0 - 147.6 μm/m-°C @Temperature 100 - 250 °C | 12.2 - 82.00 μin/in-°F @Temperature 212 - 482 °F | Average value: 98.0 μm/m-°C Grade Count:13 | |
| Specific Heat Capacity | 1.85 - 2.20 J/g-°C | 0.442 - 0.526 BTU/lb-°F | Average value: 2.12 J/g-°C Grade Count:10 |
| Thermal Conductivity | 0.240 - 0.300 W/m-K | 1.67 - 2.08 BTU-in/hr-ft2-°F | Average value: 0.261 W/m-K Grade Count:21 |
| Melting Point | 334 - 386 °C | 633 - 726 °F | Average value: 343 °C Grade Count:48 |
| Maximum Service Temperature, Air | 230 - 315 °C | 446 - 599 °F | Average value: 270 °C Grade Count:29 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 - 315 °C | 284 - 599 °F | Average value: 176 °C Grade Count:40 |
| Minimum Service Temperature, Air | -100 - -20.0 °C | -148 - -4.00 °F | Average value: -52.9 °C Grade Count:7 |
| Brittleness Temperature | -65.0 °C | -85.0 °F | Average value: -65.0 °C Grade Count:4 |
| Glass Transition Temp, Tg | 143 - 148 °C | 289 - 298 °F | Average value: 144 °C Grade Count:30 |
| UL RTI, Electrical | 260 °C | 500 °F | Average value: 260 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 180 °C | 356 °F | Average value: 180 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | Average value: 240 °C Grade Count:4 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:43 |
| Oxygen Index | 23.0 - 49.0 % | 23.0 - 49.0 % | Average value: 33.5 % Grade Count:19 |
| Glow Wire Test | 960 °C | 1760 °F | Average value: 960 °C Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 100 - 400 °C | 212 - 752 °F | Average value: 331 °C Grade Count:12 |
| Nozzle Temperature | 360 - 395 °C | 680 - 743 °F | Average value: 378 °C Grade Count:8 |
| Melt Temperature | 340 - 400 °C | 644 - 752 °F | Average value: 372 °C Grade Count:10 |
| Mold Temperature | 163 - 250 °C | 325 - 482 °F | Average value: 193 °C Grade Count:15 |
| Drying Temperature | 120 - 150 °C | 248 - 302 °F | Average value: 139 °C Grade Count:13 |
| Dry Time | 3.00 hour | 3.00 hour | Average value: 3.00 hour Grade Count:5 |
| 3.00 - 5.00 hour @Temperature 120 - 150 °C | 3.00 - 5.00 hour @Temperature 248 - 302 °F | Average value: 4.00 hour Grade Count:4 | |
| Moisture Content | 0.100 - 0.200 % | 0.100 - 0.200 % | Average value: 0.150 % Grade Count:4 |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi | Average value: 103 MPa Grade Count:3 |