- 熔體流動速率 [g/10min]: 8.5
- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.06
- 缺口沖擊強(qiáng)度: 0.88
- 斷裂伸長率 [%]: 355
- 彎曲強(qiáng)度 [MPa]: 224.0
- 彎曲模量 [MPa]: 20.2
- 硬度: 124.0
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.00030 cm/cm | 0.00030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | |
| Melt Flow | 8.5 g/10 min @Load 10.0 kg, Temperature 400 °C | 8.5 g/10 min @Load 22.0 lb, Temperature 752 °F | |
| Spiral Flow | 4.20 cm @Thickness 1.00 mm | 1.65 in @Thickness 0.0394 in | recommended processing conditions |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 107 | 107 | |
| Hardness, Rockwell R | 124 | 124 | |
| Tensile Strength, Ultimate | 224 MPa | 32500 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Yield Strength | 355 MPa | 51500 psi | |
| Flexural Modulus | 20.2 GPa | 2930 ksi | |
| Compressive Yield Strength | 240 MPa | 34800 psi | |
| Poissons Ratio | 0.44 | 0.44 | |
| Shear Modulus | 4.51 GPa | 654 ksi | Calculated |
| Shear Strength | 97.0 MPa | 14100 psi | |
| Izod Impact, Notched | 0.880 J/cm | 1.65 ft-lb/in | |
| Izod Impact, Unnotched | 4.07 J/cm | 7.62 ft-lb/in | |
| Charpy Impact, Notched | 0.750 J/cm2 | 3.57 ft-lb/in2 | |
| Coefficient of Friction, Dynamic | 0.16 | 0.16 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 μm/m-°C @Temperature 100 °C | 7.78 μin/in-°F @Temperature 212 °F | |
| 14.0 μm/m-°C @Temperature 20.0 °C | 7.78 μin/in-°F @Temperature 68.0 °F | ||
| 30.0 μm/m-°C @Temperature 250 °C | 16.7 μin/in-°F @Temperature 482 °F | ||
| Specific Heat Capacity | 1.85 J/g-°C | 0.442 BTU/lb-°F | |
| Thermal Conductivity | 0.920 W/m-K | 6.38 BTU-in/hr-ft2-°F | |
| Melting Point | 340 °C | 644 °F | |
| Maximum Service Temperature, Air | 315 °C | 599 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | |
| Brittleness Temperature | -65.0 °C | -85.0 °F | |
| Glass Transition Temp, Tg | 143 °C | 289 °F | |
| UL RTI, Mechanical with Impact | 200 °C | 392 °F | |
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 380 °C | 716 °F | Middle Barrel Temp |
| Rear Barrel Temperature | 360 °C | 680 °F | |
| Middle Barrel Temperature | 380 °C | 716 °F | |
| Front Barrel Temperature | 390 °C | 734 °F | |
| Nozzle Temperature | 390 °C | 734 °F | |
| Mold Temperature | 180 °C | 356 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3 hour | 3 hour | |