- 密度 [g/cm3]: 1.53
- 缺口沖擊強度: 1.17
- 彎曲模量 [MPa]: 10.75
- 熱變形溫度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in3 | ISO 1183 |
| 1.54 g/cc | 0.0556 lb/in3 | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 175 MPa | 25400 psi | ASTM D638 |
| 175 MPa | 25400 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 13.1 GPa | 1900 ksi | 1 mm/min; ISO 527 |
| 13.23 GPa | 1919 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
| 264 MPa | 38300 psi | ISO 178 | |
| Flexural Modulus | 10.75 GPa | 1559 ksi | ASTM D790 |
| 12.7 GPa | 1840 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m2 | 5.23 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 57.0 kJ/m2 | 27.1 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 17.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 9.44 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 18.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 10.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 48.4 μm/m-°C @Temperature -40.0 - 40.0 °C | 26.9 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 48.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 27.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| >= 298 °C @Thickness 3.20 mm | >= 568 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 298 °C @Thickness 3.20 mm | >= 568 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.780 mm | V-0 @Thickness 0.0307 in | UL 94 by SABIC-IP |