- 密度 [g/cm3]: 1.57
- 缺口沖擊強(qiáng)度: 0.8
- 彎曲模量 [MPa]: 17.34
- 熱變形溫度 [℃]: 290.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Density | 1.57 g/cc | 0.0567 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 |
| 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.00090 - 0.020 cm/cm @Time 86400 sec | 0.00090 - 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 196 MPa | 28400 psi | 5 mm/min; ISO 527 |
| 203 MPa | 29400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 41.09 GPa | 5960 ksi | 1 mm/min; ISO 527 |
| 62.98 GPa | 9134 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 296 MPa | 42900 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| 391 MPa | 56700 psi | ISO 178 | |
| Flexural Modulus | 17.34 GPa | 2515 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 36.49 GPa | 5292 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.11 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 | 3.81 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m2 | 22.4 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C | 12.5 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 290 °C @Thickness 3.20 mm | 554 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 290 °C @Thickness 3.20 mm | 554 °F @Thickness 0.126 in | unannealed; ASTM D648 | |