- 密度 [g/cm3]: 1.47
- 缺口沖擊強度: 0.58
- 拉伸強度 [MPa]: 240.0
- 彎曲模量 [MPa]: 26.88
- 熱變形溫度 [℃]: 338.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ASTM D792 |
| 1.47 g/cc | 0.0531 lb/in3 | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.00050 cm/cm @Time 86400 sec | 0.00050 in/in @Time 24.0 hour | ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec | 0.0060 - 0.0080 in/in @Time 24.0 hour | ASTM D955 |
| 0.0073 cm/cm @Time 86400 sec | 0.0073 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 240 MPa | 34800 psi | ASTM D638 |
| 242 MPa | 35100 psi | ISO 527 | |
| Tensile Strength, Yield | 240 MPa | 34800 psi | ASTM D638 |
| 242 MPa | 35100 psi | ISO 527 | |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Elongation at Yield | 1.3 % | 1.3 % | ASTM D638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Tensile Modulus | 30.52 GPa | 4427 ksi | 1 mm/min; ISO 527 |
| 33.09 GPa | 4799 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 352 MPa | 51100 psi | ISO 178 |
| 365 MPa | 52900 psi | ASTM D790 | |
| Flexural Modulus | 26.88 GPa | 3899 ksi | ASTM D790 |
| 27.5 GPa | 3990 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.04 J/cm | 13.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m2 | 19.0 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 15.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 27.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 15.0 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 7.00 μm/m-°C @Temperature -40.0 - 40.0 °C | 3.89 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 7.20 μm/m-°C @Temperature -40.0 - 40.0 °C | 4.00 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 338 °C | 640 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 338 °C @Thickness 3.20 mm | 640 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 326 °C | 619 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 322 °C @Thickness 3.20 mm | 612 °F @Thickness 0.126 in | unannealed; ASTM D648 | |