- 密度 [g/cm3]: 1.43
- 缺口沖擊強度: 0.58
- 彎曲模量 [MPa]: 10.34
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 139 MPa | 20200 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 10.34 GPa | 1500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.23 | 0.23 | ASTM D3702 Modified |
| K (wear) Factor | 24.2 x 10-8 mm3/N-M | 12.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C @Thickness 3.20 mm | 554 °F @Thickness 0.126 in | unannealed; ASTM D648 |