- 拉伸強度 [MPa]: 108.0
- 彎曲強度 [MPa]: 51.7
- 彎曲模量 [MPa]: 4.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Deformation | 0.090 % | 0.090 % | ASTM D621 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 104 | 104 | ASTM D785 | ||
| Hardness, Shore D | 88 | 88 | ASTM D2240 | ||
| Tensile Strength at Break | 96.5 MPa | 14000 psi | ASTM D368 | ||
| 29.6 MPa @Temperature 316 °C | 4300 psi @Temperature 600 °F | ||||
| Tensile Strength, Ultimate | 51.7 MPa @Temperature 149 °C | 7500 psi @Temperature 300 °F | |||
| Tensile Strength, Yield | 108 MPa | 15600 psi | ASTM D638 | ||
| Elongation at Break | 35 % | 35 % | ASTM D638 | ||
| Flexural Strength | 174 MPa | 25300 psi | ASTM D790 | ||
| 4.83 MPa @Temperature 316 °C | 700 psi @Temperature 600 °F | ||||
| 72.4 MPa @Temperature 149 °C | 10500 psi @Temperature 300 °F | ||||
| Flexural Modulus | 4.14 GPa | 600 ksi | Flexural 0.5% Secant Modulus; ASTM D790 | ||
| Compressive Strength | 131 MPa | 19000 psi | ASTM D695 | ||
| Shear Strength | 85.5 MPa | 12400 psi | Transverse; ASTM D732 | ||
| 85.5 MPa | 12400 psi | Axial; ASTM D732 | |||
| 15.9 MPa @Temperature 316 °C | 2300 psi @Temperature 600 °F | ||||
| 46.9 MPa @Temperature 149 °C | 6800 psi @Temperature 300 °F | ||||
| Secant Modulus | 4.24 GPa | 615 ksi | Tensile 0.5% Secant Modulus; ASTM D638 | ||
| Coefficient of Friction, Dynamic | 0.29 | 0.29 | PV=12600 psi-fi./min.; ASTM G77 | ||
| K (wear) Factor | 105 x 10-8 mm3/N-M | 52.0 x 10-10 in3-min/ft-lb-hr | ASTM G77 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 46.8 μm/m-°C @Temperature <=149 °C | 26.0 μin/in-°F @Temperature <=300 °F | ASTM E228 | ||
| 135 μm/m-°C @Temperature >=149 °C | 75.0 μin/in-°F @Temperature >=300 °F | ASTM E228 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | |||
| Descriptive Properties | |||||
| Color | Tan | ||||