- 缺口沖擊強度: 1.2
- 拉伸強度 [MPa]: 177.0
- 彎曲模量 [MPa]: 8.96
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 177 MPa | 25700 psi | Type I, 51 mm/min; ASTM D638 | ||
| Elongation at Break | 9.0 % | 9.0 % | Type I, 51 mm/min; ASTM D638 | ||
| Flexural Strength | 259 MPa | 37600 psi | ASTM D790 | ||
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.25 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 360 - 382 °C | 680 - 720 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 245 °C @Thickness 3.18 mm | >= 473 °F @Thickness 0.125 in | Annealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 163 - 177 °C | 325 - 351 °F | |||
| Drying Temperature | 104 °C | 219 °F | |||
| Dry Time | 3.00 hour | 3.00 hour | |||
| Descriptive Properties | |||||
| Agency Ratings | USP Class VI | ||||
| Appearance | Natural Color | ||||
| Features | Biocompatible | ||||
| Good Chemical Resistance | |||||
| Medium Impact Resistance | |||||
| Specialty Grade | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | PEEK | ||||
| Generic Name | Polyetheretherketone (PEEK) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | High Temperature Applications | ||||
| Hospital Goods | |||||
| Medical/Healthcare Applications | |||||