- 缺口沖擊強度: 0.5
- 拉伸強度 [MPa]: 90.0
- 彎曲模量 [MPa]: 3.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Volatiles | 0.50 % | 0.50 % | by TGA |
| Viscosity Test | 0.78 cm3/g | 0.78 cm3/g | Inherent, 0.5% solution in 98%H2SO4; ASTM D2857 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | >= 20 % | >= 20 % | ASTM D638 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 340 °C | 644 °F | DSC |
| Glass Transition Temp, Tg | 145 °C | 293 °F | DSC |
| Processing Properties | Metric | English | Comments |
| Moisture Content | 0.20 % | 0.20 % | P/QA/I/043 |