- 密度 [g/cm3]: 1.44
- 拉伸強度 [MPa]: 100.0
- 彎曲模量 [MPa]: 4.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527 |
| Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ASTM D638 |
| Flexural Modulus | 4.40 GPa | 638 ksi | ASTM D790 |
| Charpy Impact, Notched | 4.50 J/cm2 | 21.4 ft-lb/in2 | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 343 °C | 649 °F | DIN 53 765 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Long Term |
| 300 °C | 572 °F | Short Term | |
| Glass Transition Temp, Tg | 143 °C | 289 °F | DIN 53 765 |
| Flammability, UL94 | V-0 | V-0 | |