- 密度 [g/cm3]: 1.43
- 缺口沖擊強度: 0.294
- 彎曲模量 [MPa]: 14.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 | ||
| Filler Content | 30 % | 30 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 125 | 125 | ASTM D785 | ||
| Tensile Strength | 153.8 MPa | 22310 psi | ASTM D638 | ||
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 | ||
| 2.4 % | 2.4 % | Flexural Strain; ASTM D790 | |||
| Tensile Modulus | 19.66 GPa | 2851 ksi | ASTM D638 | ||
| Flexural Strength | 201 MPa | 29100 psi | ASTM D790 | ||
| Flexural Modulus | 14.7 GPa | 2130 ksi | ASTM D790 | ||
| Compressive Strength | 196 MPa | 28400 psi | ASTM D695 | ||
| Compressive Modulus | 4.317 GPa | 626.2 ksi | ASTM D695 | ||
| Izod Impact, Notched | 0.294 J/cm | 0.550 ft-lb/in | ASTM D256 | ||
| Descriptive Properties | |||||
| Color | Black | ||||