- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.481
- 拉伸強度 [MPa]: 186.0
- 彎曲模量 [MPa]: 12.755
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | at 24 hours; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 107 | 107 | ASTM D785 |
| Tensile Strength, Yield | 186 MPa | 27000 psi | ASTM D638 |
| Elongation at Break | 1.1 % | 1.1 % | ASTM D638 |
| Tensile Modulus | 12.999 GPa | 1885.4 ksi | 1 % Sec; ASTM D638 |
| Flexural Strength | 318 MPa | 46100 psi | ASTM D790 |
| Flexural Modulus | 12.755 GPa | 1850.0 ksi | Tangent; ASTM D790 |
| Compressive Strength | 240 MPa | 34800 psi | ASTM D695 |
| Shear Strength | 97.2 MPa | 14100 psi | Ultimate; ASTM D3846 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | 1200 in/min, 155 lbs Load; ASTM D1894-95 |
| Limiting Pressure Velocity | 13.5 MPa-m/sec | 385000 psi-ft/min | 1200 in/min |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 140000 ohm-cm | 140000 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.4 μm/m-°C @Temperature 20.0 °C | 8.00 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.918 W/m-K | 6.37 BTU-in/hr-ft2-°F | ASTM C177 |
| Melting Point | 334 °C | 633 °F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous |
| Deflection Temperature at 1.8 MPa (264 psi) | 316 °C | 600 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |