- 熔體流動速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.94
- 彎曲強度 [MPa]: 8.83
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D792 |
| Particle Mesh Size | 80 - 150 Mesh | 80 - 150 Mesh | |
| Melt Flow | 22 g/10 min @Load 10.0 kg, Temperature 230 °C | 22 g/10 min @Load 22.0 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 75 | 75 | ASTM D2240 |
| Tensile Strength, Ultimate | 8.83 MPa | 1280 psi | ASTM D412 |
| Elongation at Break | 550 % | 550 % | ASTM D412 |
| 100% Modulus | 0.04116 GPa | 5.970 ksi | ASTM D412 |
| Tear Strength | 38.2 kN/m | 218 pli | ASTM D412 |
| Compression Set | 43 % @Temperature 70.0 °C, Time 79200 sec | 43 % @Temperature 158 °F, Time 22.0 hour | ASTM D395 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 170 °C | 320 - 338 °F | Metering Temperature, Extrusion |
| Rear Barrel Temperature | 150 - 160 °C | 302 - 320 °F | Extrusion |
| 160 - 190 °C | 320 - 374 °F | Injection Molding | |
| Middle Barrel Temperature | 155 - 165 °C | 311 - 329 °F | Transition, Extrusion |
| 170 - 190 °C | 338 - 374 °F | Injection Molding | |
| Front Barrel Temperature | 170 - 180 °C | 338 - 356 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection Molding | |
| Nozzle Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Die Temperature | 170 - 180 °C | 338 - 356 °F | Extrusion |
| Melt Temperature | 150 - 180 °C | 302 - 356 °F | Extrusion |
| 160 - 200 °C | 320 - 392 °F | Injection Molding | |
| Mold Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Injection Molding |
| Injection Pressure | 5.00 - 40.0 MPa | 725 - 5800 psi | Injection Molding |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection Molding |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm | Extrusion |
| 100 - 200 rpm | 100 - 200 rpm | Injection Molding | |