- 熔體流動速率 [g/10min]: 25.5
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 0.850
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.890 g/cc | 0.890 g/cc | ISO 1183 |
| Linear Mold Shrinkage | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | as molded; ISO 294 |
| 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in | after bake; ISO 294 | |
| Melt Flow | 25.5 g/10 min | 25.5 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | 150x10x4 mm specimen, 50 mm/min; ISO 527-1/527-2 |
| Flexural Modulus | 0.850 GPa | 123 ksi | 80x10x4 mm specimen, 2 mm/min; ISO 178 |
| Impact Test | 20.0 J | 14.8 ft-lb | multiaxial, 2.2 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.8 μm/m-°C @Temperature -30.0 - 80.0 °C | 6.56 μin/in-°F @Temperature -22.0 - 176 °F | ASTM E228 |