- 熔體流動速率 [g/10min]: 54.0
- 彎曲強度 [MPa]: 7.8
- 彎曲模量 [MPa]: 0.0644
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.030 cm/cm | 0.010 - 0.030 in/in | |||
| Melt Flow | 54 g/10 min @Load 10.0 kg, Temperature 190 °C | 54 g/10 min @Load 22.0 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 83 | 83 | ISO 868 | ||
| Tensile Strength | 15.4 MPa | 2230 psi | ISO 37 | ||
| Tensile Strength, Ultimate | 7.80 MPa | 1130 psi | ISO 37 | ||
| Elongation at Break | 330 % | 330 % | ISO 37 | ||
| Flexural Strength | 4.70 MPa | 682 psi | ISO 178 | ||
| Flexural Modulus | 0.0644 GPa | 9.34 ksi | ISO 178 | ||
| Tear Strength | 60.0 kN/m | 342 pli | ISO 34 | ||
| Taber Abrasion, mg/1000 Cycles | 56 | 56 | ASTM D3389 | ||
| Compression Set | 28 % @Temperature 23.0 °C, Time 79200 sec | 28 % @Temperature 73.4 °F, Time 22.0 hour | ISO 815 | ||
| 84 % @Temperature 70.0 °C, Time 79200 sec | 84 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 165 - 175 °C | 329 - 347 °F | |||
| Middle Barrel Temperature | 170 - 180 °C | 338 - 356 °F | |||
| Front Barrel Temperature | 180 - 195 °C | 356 - 383 °F | |||
| Nozzle Temperature | 185 - 200 °C | 365 - 392 °F | |||
| Melt Temperature | 195 °C | 383 °F | |||
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| Drying Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Descriptive Properties | |||||
| Injection Speed | MED-FAST | ||||