- 彎曲強度 [MPa]: 3.2
- 彎曲模量 [MPa]: 0.0221
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.030 cm/cm | 0.010 - 0.030 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 63 | 63 | ISO 868 | ||
| Tensile Strength | 5.70 MPa | 827 psi | ISO 37 | ||
| Tensile Strength, Ultimate | 3.20 MPa | 464 psi | ISO 37 | ||
| Elongation at Break | 475 % | 475 % | ISO 37 | ||
| Flexural Strength | 1.20 MPa | 174 psi | ISO 178 | ||
| Flexural Modulus | 0.0221 GPa | 3.21 ksi | ISO 178 | ||
| Tear Strength | 25.3 kN/m | 144 pli | ISO 34 | ||
| Compression Set | 13 % @Temperature 23.0 °C, Time 79200 sec | 13 % @Temperature 73.4 °F, Time 22.0 hour | ISO 815 | ||
| 72 % @Temperature 70.0 °C, Time 79200 sec | 72 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 185 - 195 °C | 365 - 383 °F | |||
| Middle Barrel Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Front Barrel Temperature | 200 - 215 °C | 392 - 419 °F | |||
| Nozzle Temperature | 205 - 220 °C | 401 - 428 °F | |||
| Melt Temperature | 215 °C | 419 °F | |||
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |||
| Drying Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Descriptive Properties | |||||
| Injection Speed | MED-FAST | ||||