- 熔體流動速率 [g/10min]: 40.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ASTM D792 |
| Melt Flow | 40 g/10 min @Load 10.0 kg, Temperature 230 °C | 40 g/10 min @Load 22.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 72 - 78 | 72 - 78 | ASTM D2240 |
| Tensile Strength at Break | 4.41 MPa @Thickness 2.00 mm | 640 psi @Thickness 0.0787 in | 50mm/min; ASTM D638 |
| Elongation at Break | 300 % @Thickness 2.00 mm | 300 % @Thickness 0.0787 in | 50mm/min; ASTM D638 |
| Izod Impact, Notched | NB @Thickness 6.40 mm, Temperature 23.0 °C | NB @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 |
| NB @Thickness 6.40 mm, Temperature -40.0 °C | NB @Thickness 0.252 in, Temperature -40.0 °F | ASTM D256 | |
| Tear Strength | 29.4 kN/m | 168 pli | 50mm/min, @ Break; ASTM D624 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 200 - 240 °C | 392 - 464 °F | Injection Molding |
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |