| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 and ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 74 @Time 15.0 sec | 74 @Time 0.00417 hour | 2 mm; ISO 868 | ||
| Tensile Strength at Break | 11.7 MPa | 1700 psi | Across Flow; ASTM D412 and ISO 37 | ||
| Tensile Stress | 3.20 MPa @Strain 100 % | 464 psi @Strain 100 % | Across Flow; ASTM D412 and ISO 37 | ||
| Elongation at Break | 570 % | 570 % | Across Flow; ASTM D412 and ISO 37 | ||
| Tear Strength | 46.0 kN/m | 262 pli | Across Flow, Die C; ASTM D624 | ||
| 46.0 kN/m | 262 pli | Across Flow, Method Bb, Angle (Nicked); ISO 34-1 | |||
| Compression Set | 37 % @Temperature 23.0 °C, Time 79200 sec | 37 % @Temperature 73.4 °F, Time 22.0 hour | ASTM D395B Type 1 and ISO 188 Type A | ||
| 68 % @Temperature 70.0 °C, Time 79200 sec | 68 % @Temperature 158 °F, Time 22.0 hour | ASTM D395B Type 1 and ISO 188 Type A | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL File Number - E80017 | ||
| HB @Thickness 2.10 mm | HB @Thickness 0.0827 in | ||||
| Descriptive Properties | |||||
| Change in Tensile Strength in Air | -8.0% | ASTM D573, 100°C, 168 hr | |||
| Change in Ultimate Elongation in Air | -11% | ASTM D573, 100°C, 168 hr | |||