- 脆化溫度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 78 | 78 | Air at 302°F, 168 hr; ASTM D573 | ||
| 83 | 83 | 2 mm, 15 sec; ISO 868 | |||
| Tensile Strength at Break | 8.031 MPa | 1165 psi | Air at 302°F, 168 hr; ASTM D573 | ||
| 8.83 MPa | 1280 psi | Across Flow; ASTM D412 | |||
| Tensile Stress | 3.50 MPa @Strain 100 % | 508 psi @Strain 100 % | Across Flow; ASTM D412 | ||
| Elongation at Break | 450.8 % | 450.8 % | Air at 302°F, 168 hr; ASTM D573 | ||
| 460 % | 460 % | Across Flow; ASTM D412 | |||
| Tear Strength | 24.0 kN/m | 137 pli | 73°F, Die C, Across Flow; ASTM D624 | ||
| Compression Set | 33 % | 33 % | 158°F, 22 hr; ASTM D395 | ||
| 42 % | 42 % | 257°F, 70 hr; ASTM D395 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.7 | 2.7 | 1.98 mm; ASTM D150 | ||
| Dielectric Strength | 27.2 kV/mm | 690 kV/in | 2.03 mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | |||
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 | ||
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Die Temperature | 204 °C | 400 °F | Extrusion | ||
| Melt Temperature | 177 - 204 °C | 350 - 400 °F | Extrusion | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Back Pressure | 5.00 - 20.0 MPa | 725 - 2900 psi | Extrusion | ||
| Descriptive Properties | |||||
| Change in Mass in IRM 903 Oil at 257°F for 70 hr | 45 | ||||
| Color | Black | ||||
| Form | Pellets | ||||