- 彎曲強度 [MPa]: 6.48
- 脆化溫度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 87 | 87 | .12 in; ASTM D2240 | ||
| Tensile Strength at Break | 8.736 MPa | 1267 psi | 257°F, 70 hr, in IRM 903 Oil; ASTM D471 | ||
| 10.608 MPa | 1538.5 psi | Air at 302°F, 168 hr; ASTM D573 | |||
| 12.5 MPa | 1810 psi | Across Flow; ASTM D412 | |||
| Tensile Strength, Ultimate | 6.48 MPa | 940 psi | Across Flow; ASTM D412 | ||
| Elongation at Break | 290.7 % | 290.7 % | 257°F, 70 hr, in IRM 903 Oil; ASTM D471 | ||
| 387.6 % | 387.6 % | Air at 302°F, 168 hr; ASTM D573 | |||
| 510 % | 510 % | Across Flow; ASTM D412 | |||
| Compression Set | 32 % | 32 % | 158°F, 22 hr; ASTM D395 | ||
| 63 % | 63 % | 257°F, 70 hr; ASTM D395 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.6 | 2.6 | ASTM D150 | ||
| Dielectric Strength | 31.5 kV/mm | 800 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | |||
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Rear Barrel Temperature | 177 - 193 °C | 350 - 380 °F | |||
| Middle Barrel Temperature | 179 - 199 °C | 355 - 390 °F | |||
| Front Barrel Temperature | 179 - 204 °C | 355 - 400 °F | |||
| Nozzle Temperature | 191 - 229 °C | 375 - 445 °F | |||
| Melt Temperature | 193 - 241 °C | 380 - 465 °F | Processing | ||
| Mold Temperature | 10.0 - 51.7 °C | 50.0 - 125 °F | Processing | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Moisture Content | 0.080 % | 0.080 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Processing | ||
| Clamp Pressure | 41.4 - 68.9 MPa | 6000 - 10000 psi | |||
| Vent Depth | 0.00254 cm | 0.00100 in | |||
| Cushion | 0.317 - 0.635 cm | 0.125 - 0.250 in | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | |||
| Descriptive Properties | |||||
| Change in Mass in IRM 903 Oil at 257°F for 70 hr | 84 | ||||
| Color | Black | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Maximum Regrind % | 20 | ||||
| Screw Compression Ratio | 2:1 - 2.5:1 | ||||
| Screw L/D Ratio | 16:1 - 20:1 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.