- 彎曲強度 [MPa]: 2.96
- 脆化溫度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 67 | 67 | .12 in; ASTM D2240 | ||
| 71 | 71 | Air at 302°F, 168 hr; ASTM D573 | |||
| Tensile Strength at Break | 4.279 MPa | 620.6 psi | 257°F, 70 hr, in IRM 903 Oil; ASTM D471 | ||
| 6.64 MPa | 963 psi | Air at 302°F, 168 hr; ASTM D573 | |||
| 7.38 MPa | 1070 psi | Across Flow; ASTM D412 | |||
| Tensile Strength, Ultimate | 2.96 MPa | 430 psi | Across Flow; ASTM D412 | ||
| Elongation at Break | 202.5 % | 202.5 % | 257°F, 70 hr, in IRM 903 Oil; ASTM D471 | ||
| 445.5 % | 445.5 % | Air at 302°F, 168 hr; ASTM D573 | |||
| 450 % | 450 % | Across Flow; ASTM D412 | |||
| Tear Strength | 22.1 kN/m | 126 pli | 73°F, Die C; ASTM D624 | ||
| Compression Set | 30 % | 30 % | 158°F, 22 hr; ASTM D395 | ||
| 41 % | 41 % | 257°F, 70 hr; ASTM D395 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.6 | 2.6 | ASTM D150 | ||
| Dielectric Strength | 28.3 kV/mm | 720 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | |||
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Die Temperature | 204 °C | 400 °F | Extrusion | ||
| Melt Temperature | 177 - 204 °C | 350 - 400 °F | Extrusion | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Back Pressure | 5.00 - 20.0 MPa | 725 - 2900 psi | Extrusion | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Pellets | ||||