- 熔體流動速率 [g/10min]: 10.0
- 拉伸強度 [MPa]: 25.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg | 10 g/10 min @Load 47.6 lb | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | ASTM D2240 |
| Tensile Strength, Yield | 25.05 MPa | 3633 psi | ASTM D412 |
| Elongation at Break | 455 % | 455 % | ASTM D412 |
| 100% Modulus | 0.00581 GPa | 0.843 ksi | ASTM D412 |
| 300% Modulus | 0.01302 GPa | 1.889 ksi | ASTM D412 |
| Tear Strength | 55.0 kN/m | 314 pli | ASTM D624 (die C) |
| Abrasion | 30 | 30 | [mm^3]; DIN 53.516 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 275 - 290 °C | 527 - 554 °F | MQSA 111 |
| Glass Transition Temp, Tg | -33.3 °C | -28.0 °F | DIN 51.007 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 185 - 205 °C | 365 - 401 °F | |
| Zone 2 | 190 - 210 °C | 374 - 410 °F | |
| Zone 3 | 195 - 215 °C | 383 - 419 °F | |
| Zone 4 | 190 - 210 °C | 374 - 410 °F | |
| Die Temperature | 185 - 205 °C | 365 - 401 °F | |