- 密度 [g/cm3]: 1.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 | ||
| Melt Index of Compound | 150 g/10 min @Load 21.6 kg, Temperature 190 °C | 150 g/10 min @Load 47.6 lb, Temperature 374 °F | cm3/10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 82 | 82 | ASTM D2240 | ||
| Hardness, Shore D | 35 | 35 | ASTM D2240 | ||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | DIN 53504 | ||
| Elongation at Break | 700 % | 700 % | DIN 53504 | ||
| 100% Modulus | 0.00350 GPa | 0.508 ksi | DIN 53504 | ||
| 300% Modulus | 0.00750 GPa | 1.09 ksi | DIN 53504 | ||
| Tear Strength | 35.0 kN/m | 200 pli | ISO 34-1 | ||
| Abrasion | 40 | 40 | mm3; ISO 4549 | ||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | V-0 | V-0 | Non-Halogen FR | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | ||
| Front Barrel Temperature | 160 - 200 °C | 320 - 392 °F | Extrusion | ||
| Nozzle Temperature | 170 - 205 °C | 338 - 401 °F | Extrusion | ||
| 200 - 210 °C | 392 - 410 °F | Injection | |||
| Adapter Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion | ||
| Die Temperature | 175 - 205 °C | 347 - 401 °F | Extrusion | ||
| Melt Temperature | 190 - 205 °C | 374 - 401 °F | Injection | ||
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection | ||
| Descriptive Properties | |||||
| Heating Zone | 170-210°C | Injection | |||