- 熔體流動速率 [g/10min]: 10.0
- 拉伸強度 [MPa]: 23.06
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg | 10 g/10 min @Load 47.6 lb | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 88 | 88 | ASTM D2240 |
| Tensile Strength, Yield | 23.06 MPa | 3344 psi | ASTM D412 |
| Elongation at Break | 415 % | 415 % | ASTM D412 |
| 100% Modulus | 0.005502 GPa | 0.7980 ksi | ASTM D412 |
| 300% Modulus | 0.0160 GPa | 2.32 ksi | ASTM D412 |
| Abrasion | 35 | 35 | [mm^3]; DIN 53.516 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 - 135 °C | 257 - 275 °F | MQSA 114 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 165 - 175 °C | 329 - 347 °F | |
| Zone 2 | 175 - 185 °C | 347 - 365 °F | |
| Zone 3 | 185 - 195 °C | 365 - 383 °F | |
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |
| Die Temperature | 190 - 200 °C | 374 - 392 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | MQSA 44 |