- 熔體流動(dòng)速率 [g/10min]: 50.0
- 密度 [g/cm3]: 1.12
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D995 | ||
| Melt Flow | 50 - 80 g/10 min | 50 - 80 g/10 min | Melt Volume Rate (cm3/10 min) | ||
| Melt Index of Compound | 55 g/10 min @Load 21.6 kg, Temperature 190 °C | 55 g/10 min @Load 47.6 lb, Temperature 374 °F | cm3/10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 85 | 85 | ASTM D2240 | ||
| Hardness, Shore D | 36 | 36 | ASTM D2240 | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | DIN 53504 | ||
| Elongation at Break | 610 % | 610 % | ASTM D412 | ||
| 100% Modulus | 0.00700 GPa | 1.02 ksi | DIN 53504 | ||
| 300% Modulus | 0.0120 GPa | 1.74 ksi | DIN 53504 | ||
| Rebound | 36 % | 36 % | Bayshore; ASTM D2632 | ||
| Tear Strength | 101 kN/m | 574 pli | ASTM D624 | ||
| Abrasion | 25 | 25 | [mm3]; ISO 4649 | ||
| Compression Set | 20 % @Temperature 23.0 °C, Time 252000 sec | 20 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 | ||
| 40 % @Temperature 70.0 °C, Time 86400 sec | 40 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 150 - 170 °C | 302 - 338 °F | Huntsman/TMA | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | ||
| Front Barrel Temperature | 160 - 200 °C | 320 - 392 °F | Extrusion | ||
| Nozzle Temperature | 200 - 210 °C | 392 - 410 °F | Injection | ||
| Adapter Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion | ||
| Die Temperature | 175 - 205 °C | 347 - 401 °F | Extrusion | ||
| Melt Temperature | 190 - 205 °C | 374 - 401 °F | Injection | ||
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection | ||
| Descriptive Properties | |||||
| Heating Zone | 170-210°C | Injection | |||