- 密度 [g/cm3]: 1.21
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D995 |
| Melt Index of Compound | 65 g/10 min @Load 0.0000102 kg, Temperature 190 °C | 65 g/10 min @Load 0.0000220 lb, Temperature 374 °F | cm3/10 min |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 86 | 86 | ASTM D2240 |
| Hardness, Shore D | 36 | 36 | ASTM D2240 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | DIN 53504 |
| Elongation at Break | 700 % | 700 % | ASTM D412 |
| 100% Modulus | 0.00590 GPa | 0.856 ksi | DIN 53504 |
| 300% Modulus | 0.0112 GPa | 1.62 ksi | DIN 53504 |
| Rebound | 35 % | 35 % | Bayshore; ASTM D2632 |
| Tear Strength | 103 kN/m | 590 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm3]; ISO 4649 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec | 25 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 50 % @Temperature 70.0 °C, Time 86400 sec | 50 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 145 - 160 °C | 293 - 320 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 170 - 195 °C | 338 - 383 °F | Extrusion |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Adapter Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Die Temperature | 175 - 205 °C | 347 - 401 °F | Extrusion |
| Roll Temperature | 160 - 180 °C | 320 - 356 °F | Front |
| 160 - 180 °C | 320 - 356 °F | Rear | |