- 密度 [g/cm3]: 1.13
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | DIN 53504 |
| Elongation at Break | 470 % | 470 % | ASTM D412 |
| 100% Modulus | 0.0123 GPa | 1.78 ksi | DIN 53504 |
| 300% Modulus | 0.0308 GPa | 4.47 ksi | DIN 53504 |
| Rebound | 35 % | 35 % | Bayshore; ASTM D2632 |
| Tear Strength | 105 kN/m | 600 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm3]; ISO 4649 |
| Compression Set | 29 % @Temperature 23.0 °C, Time 252000 sec | 29 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 82 % @Temperature 70.0 °C, Time 86400 sec | 82 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 - 188 °C | 347 - 370 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |