- 密度 [g/cm3]: 1.12
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 71 | 71 | ASTM D2240 |
| Hardness, Shore D | 22 | 22 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | DIN 53504 |
| Elongation at Break | 900 % | 900 % | ASTM D412 |
| 100% Modulus | 0.00390 GPa | 0.566 ksi | DIN 53504 |
| 300% Modulus | 0.00980 GPa | 1.42 ksi | DIN 53504 |
| Rebound | 58 % | 58 % | Bayshore; ASTM D2632 |
| Tear Strength | 70.1 kN/m | 400 pli | ASTM D624 |
| Abrasion | 60 | 60 | [mm3]; ISO 4649 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec | 25 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 48 % @Temperature 70.0 °C, Time 86400 sec | 48 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 - 164 °C | 230 - 327 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |