- 密度 [g/cm3]: 0.95
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 620 % | 620 % | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Peel Strength | 3.40 - 10.2 kN/m | 19.4 - 58.2 pli | to ABS; Renault test D41 1916 | ||
| 4.70 - 10.0 kN/m | 26.8 - 57.1 pli | to PC; Renault test D41 1916 | |||
| Graves Tear Strength | 45.0 kN/m | 257 pli | DIN ISO 34-1 Method B (b) | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 13 % | 13 % | ASTM D1003-97 | ||
| Transmission, Visible | 90 % | 90 % | ASTM D1003-97 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 - 250 °C | 392 - 482 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 sec | 176 °F @Time 2.00 hour | |||
| Descriptive Properties | |||||
| Clarity | 93% | ASTM D1003-97 | |||
| Color | Transparent | ||||