- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 | 40 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 2.60 MPa | 377 psi | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 600 % | 600 % | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Peel Strength | 1.50 kN/m | 8.56 pli | to PETG; Renault test D41 1916 | ||
| 3.00 kN/m | 17.1 pli | to ABS; Renault test D41 1916 | |||
| 10.0 kN/m | 57.1 pli | to PC; Renault test D41 1916 | |||
| Graves Tear Strength | 10.3 kN/m | 58.8 pli | DIN ISO 34-1 Method B (b) | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 - 250 °C | 392 - 482 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 sec | 176 °F @Time 2.00 hour | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Hard/Soft (N/mm) | 1.5 | with PETG; According to Renault Test D 41-1916 | |||
| 1.5 | with PBT; According to Renault Test D 41-1916 | ||||
| 10 | with PC; According to Renault Test D 41-1916 | ||||
| 3 | with ABS; According to Renault Test D 41-1916 | ||||