- 密度 [g/cm3]: 1.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 80 | 80 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 6.00 MPa | 870 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 400 % | 400 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Peel Strength | 5.00 kN/m | 28.5 pli | to ABS; Renault test D41 1916 | ||
| 5.50 kN/m | 31.4 pli | to PC/ABS; Renault test D41 1916 | |||
| 15.0 kN/m | 85.6 pli | to PC; Renault test D41 1916 | |||
| Graves Tear Strength | 25.0 kN/m | 143 pli | DIN ISO 34-1 Method B (b) | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 180 - 250 °C | 356 - 482 °F | Adhesion to engineering thermoplastics | ||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C @Time 7200 - 14400 sec | 140 - 176 °F @Time 2.00 - 4.00 hour | Pre drying | ||
| Descriptive Properties | |||||
| Color | Black | ||||