- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 80 | 80 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 8.20 MPa | 1190 psi | DIN 53504 / ISO 37 | ||
| Elongation at Break | 400 % | 400 % | DIN 53504 / ISO 37 | ||
| Peel Strength | 8.00 kN/m | 45.6 pli | to PA 6.6; Renault test D41 1916 | ||
| 24.0 kN/m | 137 pli | to PA 6; Renault test D41 1916 | |||
| Graves Tear Strength | 20.0 kN/m | 114 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 21 % @Temperature 23.0 °C, Time 259000 sec | 21 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 37 % @Temperature 70.0 °C, Time 79200 sec | 37 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 58 % @Temperature 100 °C, Time 79200 sec | 58 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | adhesion to PA 6 | ||
| 255 - 280 °C | 491 - 536 °F | adhesion to PA 6.6 and polyamide | |||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C @Time 7200 - 14400 sec | 140 - 176 °F @Time 2.00 - 4.00 hour | Pre drying | ||
| Descriptive Properties | |||||
| Color | Natural | ||||