- 密度 [g/cm3]: 1.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 3.00 MPa | 435 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 450 % | 450 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Peel Strength | 14.0 kN/m | 79.9 pli | to PA 6.6; Renault test D41 1916 | ||
| 16.0 kN/m | 91.3 pli | to PA 6; Renault test D41 1916 | |||
| Graves Tear Strength | 16.0 kN/m | 91.3 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 28 % @Temperature 23.0 °C, Time 259000 sec | 28 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 80 % @Temperature 70.0 °C, Time 79200 sec | 80 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 81 % @Temperature 100 °C, Time 79200 sec | 81 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | adhesion to PA 6 | ||
| 255 - 280 °C | 491 - 536 °F | adhesion to PA 6.6 and polyamide | |||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C @Time 7200 - 14400 sec | 140 - 176 °F @Time 2.00 - 4.00 hour | Pre drying | ||
| Descriptive Properties | |||||
| Color | Black | ||||